Subject: Re: Nihard4

Date: 10/04/01 at 5:12 AM
Posted by: Ramin_Pejman
E-mail: picitech@yahoo.com
Message Posted:

In Reply to: Re: Nihard4 posted by Arun Rao on 10/03/01 at 12:19 PM:

Dear sir
Thanks for your advise ,please be informed that we revealed retained austenite (about 60%) & heattreatment is impossible for us .
if you have any recomendations inregards with correction our analize,please be kind &advise me.
awaiting for your kind reply.
Best regards